Scrap For Aluminium casting

Product Details:

• Appearance- Aluminium frag 2-30mm
• Pyrolised
• Composition(chemical /
• physical)-                   Cu 1-4% Zn 1-3% Si=1% Fe=0.9% Mg<0.1%
•                                  Inox <0.5% Other Impurities = 0%
• Yield - 86% s.t. oven and techniques

• Appearance and description
• CLEAN OR PAINTED SLABS / FRAG LOOSE OR IN BALES
• RAW or PAINTED or ANODISED

• Composition (chemical - physical)
• Al Alloys 1000 3000 5000 6000 8000 ONE-ALLOY or MIXED FROM
• Yield PRIMARY-94% TO 98%, s.t. oven and techniques

• Appearance  - SCRAPS or SHREDDED or INCINERATORS
• Thickness     - variable 
• Composition - different alloys: 304 316 and others

• Appearance-different shapes and formats 
• Thickness-variable
• Composition- compositions to be specified

• Appearance -SCRAPS or FRAG or INCINERATOR
• Thickness -VARIABLE
• Composition -different alloys: 430 and others

Product Details:

• Appearance  -  plastic Hydraulic tubes plastic tubes for AC with Al core whole coils or frag  
• Thickness     -  Variable 
• Composition -  Primary Al alloy
•                       Al: 27-55% rest is plastic

Product Details:

• Appearance -painted foil
• Thickness -variable between 30 ad 200 micron
• Yield - 70-80% s.t. oven and techniques
• Composition-8000 Alloy Fe=1% Al 98.5% others are minor Paint between 5% and 20%

• Appearance  -  Pressed bales from old UBC with attachments to be separated 
• Composition - 3000 / 5000
•                     Attachment 10-30% all impurities

• Appearance  - DIFFERENT SIZES from 7 to 15cm
• Density        - VARIABLE
• Composition -one-alloy composition e.g. 47100, 5000 series, alloy… humidity<5%
• Yield            -over 90% s.t. oven and techniques

• Appearance  - new caps or used caps; plastic lining plus ring 
• Thickness     - variable
• Composition - 3000 alloys
•                      Al 65% rest is plastic and paint

• Appearance  - SMALL STONES from INCINERATORS (0.5-3 cm)
• Composition - Si 3% Fe 0.6% Cu 0.5% Mg 0.1% Zn 0.7% 
• Yield            - 90-94% s.t. oven and techniques

• Appearance - Aluminum frag 5-15cm
• Composition -  Si: 0.5-1.5 Fe<0.4% Cu<0.3% Zn<0.3% Mg<0.7%
• Yield - 90-92% s.t. oven and techniques

• Appearance-  tubes with plastic cap and painted aluminium body
• NEW post industrial, from toothpaste and/or tomato
• 
  
• Thickness -  variable
• 
  
• Composition -  Al99.7%
• Al 75% Plastic 20% Paint 5%
• 
  
• Yield - after removing caps, aluminium is pure
• s.t. oven and techniques